Synthesis of Polyacrylic/Silica Nanocomposite Latexes using Static Mixer

Gholamali Farzi (1) , Elodie Bourgeat-Lami (1) , Timothy Mckenna (1)

1 LCPP

Static mixers (Sulzer Chemtech; SMX) were used to prepare silica/MMA-co-BA miniemulsions that were polymerized to produce nanocomposite latexes. Acceptable conditions for the formulation of polymerizable nanodroplets were found and subsequently used to produce silica/poly(MMA-co-BA) nanocomposites. The droplet size distribution of the resulting miniemulsions was narrow enough that it could be successfully polymerized. It was found that the droplet size depends on the silica content and increases with increasing the silica concentration. It was also shown that there is a relationship between the droplet size and the viscosity of the dispersed phase. The majority of droplets were nucleated upon polymerization when less than 15% silica was used. However, when the silica content exceeded 15%, the ratio of the number of particles in the final latex to the number of droplets (Np/Nd) increased to value much higher than 1 indicating the occurrence of homogeneous nucleation.

Mots clés: static mixer; droplet size; miniemulsion; nanocomposite; particle size

Mots clés: silica

Domaines: Polymères

Gholamali Farzi, Elodie Bourgeat-Lami, Timothy Mckenna. Synthesis of Polyacrylic/Silica Nanocomposite Latexes using Static Mixer. Macromolecular Symposia, 2010, 289, pp.129-134. ⟨10.1002/masy.200900015⟩. ⟨hal-00723802⟩